Preparation and Its Performance of Rectorite/Poly(Sodium Acrylate-Co-Acrylamide) Superabsorbent Composite
-
摘要: 采用焙烧-磁选法、酸洗提纯法、煅烧法均能有效减少湖北钟祥累托石粘土中的黄铁矿.实验用累托石粘土中黄铁矿含量为4.37%, 硫含量为2.32%.采用焙烧磁选法, 温度300℃、时间2.0h、二次磁选后, 累托石粘土中硫含量降为0.52%;酸洗法, 酸液浓度60%、时间1.0h、温度60℃时, 硫含量为0.57%;煅烧法, 当温度550℃、时间为0.5h时, 硫含量为0.78%.研究发现所得粘土矿物对聚合复合法制备累托石/聚丙稀酰胺-丙烯酸(钠) 吸水保水复合材料的阻聚作用不明显, 且不影响后续聚合反应最高硫含量约为0.78%.在65~70℃反应条件下, 含煅烧累托石粘土20%、丙烯酰胺15%、引发剂0.25%、交联剂0.08%, 丙烯酸中和度为80%的吸水保水复合材料的吸去离子水倍率为870, 吸自来水倍率为250, 吸生理盐水倍率为68.累托石粘土添加量在0%~30%之间时, 吸水保水复合材料的吸液倍率比不含累托石的吸水树脂高.吸水保水复合材料吸液倍率从870g/g降到84g/g时, 凝胶强度从49g/cm2上升到235g/cm2.Abstract: The effect of three different types of purification processes (roasting-magnetic dressing, acid pickling and calcining) on the sulfur content of rectorite clay (pyrite content 4.37%, sulfur content 2.32%) was investigated. By roasting-magnetic dressing, the sulfur content was reduced to 0.52% when roasting at 300 ℃ for 2 h and magnetic dressing twice; By acid pickling, the sulfur content remained 0.57% under the condition of 60 ℃ and acid pickling for 1 h with 60% nitric acid solution; By calcining, 0.78% of sulfur was left if calcined for 0.5 h at 550 ℃. The experimental results indicate there is no obvious inhibition effect (corresponding maximal sulfur content 0.78%) when rectorite/poly (sodium acrylate-Co-acrylamide) is synthesized by in-situ aqueous solution polymerization with the purified rectorite clay as material. At 65-70 ℃, the water absorbencies (WA) of superabsorbent composite (containing 20% purified rectorite clay, 15% acrylamide, 0.25% initiator and 0.08% cross linker, with the neutralization degree of acrylic acid being 80%) in distilled water, tap water and 0.9% NaCl (aq) are 870, 250 and 68 respectively. When the content of rectorite is between 0%-30%, WA of superabsorbent composite is higher than that of superabsorbent resin that contains no rectorite. When WA of superabsorbent composite in distilled water is reduced from 870 g/g to 84 g/g, its gel strength rises from 49 g/cm2 to 235 g/cm2.
-
Key words:
- rectorite /
- pyrite /
- purification /
- superabsorbent composite /
- preparation /
- performance
-
图 1 交联剂用量(a)、丙烯酰胺用量(b)和中和度(c)对吸液倍率的影响
Fig. 1. Effect of cross linking agent (a), acrylamide (b) and neutralization degree of monomer (c) on water absorbency
图 2 引发剂用量(a)和累托石添加量(b)对吸液倍率的影响
Fig. 2. Effect of concentration of initiator (a) and concentration of rectorite (b) on water absorbency
表 1 先焙烧后磁选除黄铁矿的效果
Table 1. Effect of sulfur removed by roasting-magnetic dressing
表 2 酸洗法去黄铁矿实验结果
Table 2. Effects of sulfur removed by nitric acid pickling
表 3 不同锻烧条件下累托石粘土中硫含量
Table 3. Sulfur contents under different burned conditions
表 4 累托石粘土中硫含量对生成凝胶的影响
Table 4. Effect of sulfur content in rectorite on gel formation
-
[1] Fan, L. R., Xu, Z. L., Shen, S. Y., 2005. Research progress in mineral/polymer superabsorbent composites. Journal of Functional Materials, 36 (12): 1827-1830 (in Chinese). [2] Guo, B. W., Xiao, Y., 1990. Method of mineral separationand technology. China University of Geosciences Press, Wuhan, 251-253 (in Chinese). [3] Jiang, T., Liu, Y. J., 1989. Rectorite. Hubei Sci. Tech. Press, Wuhan, 116-136 (in Chinese). [4] Wang, C. L., Fan, L. R., Shen, S. Y., et al., 2005. Preparation of mineral/acrylate superabsorbent resin by rectorite. J. Wuhan Inst. Chem Tech. , 27 (1): 46-48 (in Chinese with English abstract). [5] Xu, Z. L., Fan, L. R., Shen, S. Y., et al., 2004. Influence of Ca2+ surface crosslinking on properties of mont morillonite/polyacrylate superabsorbent composite. Functional Material, 35 (9): 2596-2598 (in Chinese with English abstract). [6] Ye, H., Zhao, J. Q., Zhang, Y. H., 2004. Novel degradable superabsorbent materials of silicate/acrylic-based polymer hybrids. Journal of Applied Polymer Science, 91: 936-940. doi: 10.1002/app.13274 [7] Yuan, J. Z., Yan, Q. X., Zhang, L. Y., et al., 2004. Purification of rectorite. Nonmetallic Mines, 27 (2): 33-35 (in Chinese with English abstract). [8] Zhang, F. S., Gao, C. D., Zhang, W., et al., 2004. Studied on the liquid absorption rate of super water absorption polymer and its measurement method. Polymer Materials Science and Engineering, 20 (1): 179-183 (in Chinese with English abstract). [9] Zou, X. X., 1991. Superabsorbent. Chemical Industry Press, Beijing, 385-386 (in Chinese). [10] 范力仁, 徐志良, 沈上越, 2005. 非金属矿物/高分子吸水保水复合材料研究进展. 功能材料, 36 (12): 1827-1830. doi: 10.3321/j.issn:1001-9731.2005.12.004 [11] 郭秉文, 肖云, 1990. 选矿方法与工艺实践. 武汉: 中国地质大学出版社, 251-253. [12] 江涛, 刘源骏, 1989. 累托石. 湖北科学技术出版社, 116-136. [13] 王春龙, 范力仁, 沈上越, 等, 2005. 用累托石制备矿物/聚丙烯酸盐高吸水树脂. 武汉化工学院学报, 27 (1): 46-48. doi: 10.3969/j.issn.1674-2869.2005.01.014 [14] 徐志良, 范力仁, 沈上越, 等, 2004. 表面Ca2+交联对蒙托石-聚丙烯酸钠性能的影响. 功能材料, 35 (9): 2596-2598. https://cpfd.cnki.com.cn/Article/CPFDTOTAL-GNCL200409002136.htm [15] 袁继祖, 晏全香, 张凌燕, 等, 2004. 高纯累托石提纯试验研究. 非金属矿, 27 (2): 33-35. doi: 10.3969/j.issn.1000-8098.2004.02.012 [16] 张付舜, 高程达, 张伟, 等, 2004. 高吸水树脂吸液率及其测定方法的研究. 高分子材料科学与工程, 20 (1): 179-183. doi: 10.3321/j.issn:1000-7555.2004.01.047 [17] 邹新禧, 1991. 超强吸水剂. 北京: 化学工业出版社, 385-386. -